General Properties |
FS 3300PA PA1212-based powder |
FS 3300PA PA1212-based powder |
FS 3401GB
Glass bead filled |
FS 3400CF
Carbon fiber filled |
FS 3250MF
Mineral fiber filled |
FS 4100PA
PA11 powder |
|
Bulk Density |
0.45~0.55 g/cm³ |
0.48 g/cm³ |
0.67 g/cm³ |
0.51 g/cm³ |
0.55 g/cm³ |
0.49 g/cm³ |
|
Part Density |
0.96 g/cm³ |
0.95 g/cm³ |
1.26 g/cm³ |
1.08-1.10 g/cm³ |
1.20 g/cm³ |
1.03 g/cm³ |
|
Color |
Black |
White |
Gray |
Black |
Light gray |
White |
|
|
|
|
|
|
|
|
|
Thermal Properties |
|
|
|
|
|
|
|
Melting Point (10℃/min) ISO 11357.1:1997 |
179~185°C |
183°C |
184°C |
184°C |
183°C |
203°C |
|
Heat Deflection Temp(HDT) @1.82 MPa ISO 75-2:2003 |
70~85°C |
83.5°C |
68.8°C |
72 °C |
129°C |
49°C |
|
Heat Deflection Temp(HDT) @0.45 MPa ISO 75-2:2003 |
135~155°C |
146.2°C |
152.4°C |
168 °C |
171°C |
150°C |
|
|
|
|
|
|
|
|
|
Mechanical Properties |
|
|
|
|
|
|
|
Tensile Strength ISO 527.2:1993 |
40~50 MPa |
46 MPa |
44 MPa |
65-70 MPa |
51 MPa |
49 MPa |
|
Tensile Modulus ISO 527.2:1993 |
1700~1900 MPa |
1602 MPa |
2644 MPa |
4700-6500 MPa |
6130 MPa |
1542 MPa |
|
Elongation at Break ISO 527.2:1993 |
5~20% |
36% |
9.3% |
3.0-4.0% |
5% |
58% |
|
Flexural Strength ISO 178:2001 |
36~45 MPa |
46.3 MPa |
60.3 MPa |
94-113 MPa |
76 MPa |
60 MPa |
|
Flexural Modulus ISO 178:2001 |
1000~1150 MPa |
1300 MPa |
2210 MPa |
4500-5600 MPa |
4633 MPa |
1463 MPa |
|
Izod Impact Strength (notched) ISO 180:2000 |
10~24 KJ/m² |
4.9 KJ/m² |
6.6 KJ/m² |
4.3 KJ/m² |
5.59 KJ/m² |
25 KJ/m² |
|
Izod Impact Strength (unnotched) ISO 180:2000 |
Tbd |
13.2 KJ/m² |
31.1 KJ/m² |
16 KJ/m² |
20.78 KJ/m² |
No break |
|
General Properties |
Ultrasint X043
PA6 powder |
Ultrasint X028
PA6 powder |
FS 8100PPS
PPS powder |
FS 1092A-TPU
TPU powder |
FS 1088A-TPU
TPU powder |
|
Bulk Density |
0.52g/cm³ |
0.52 g/cm³ |
0.57 g/cm³ |
0.64 g/cm³ |
0.46 g/cm³ |
|
Part Density |
1.14g/cm³ |
1.15 g/cm³ |
1.28 g/cm³ |
1.12 g/cm³ |
1.20 g/cm³ |
|
Color |
Black |
Light yellow |
Light yellow |
White |
White |
|
|
|
|
|
|
|
|
Thermal Properties |
|
|
|
|
|
|
Melting Point (10℃/min) ISO 11357.1:1997 |
225°C |
220°C |
295°C |
169°C |
160°C |
|
Heat Deflection Temp(HDT) @1.82 MPa ISO 75-2:2003 |
93°C |
100°C |
116 °C |
n/a |
n/a |
|
Heat Deflection Temp(HDT) @0.45 MPa ISO 75-2:2003 |
191°C |
199°C |
220°C |
n/a |
n/a |
|
|
|
|
|
|
|
|
Mechanical Properties |
|
|
|
|
|
|
Tensile Strength ISO 527.2:1993 |
74 MPa |
78MPa |
47 MPa |
18 MPa |
20 MPa |
|
Tensile Modulus ISO 527.2:1993 |
3457 MPa |
3550 MPa |
3412 MPa |
61 MPa |
30MPa |
|
Elongation at Break ISO 527.2:1993 |
4.0% |
13.0% |
3.8% |
276% |
340% |
|
Flexural Strength ISO 178:2001 |
99 MPa |
121 MPa |
63 MPa |
6.2 MPa |
n/a |
|
Flexural Modulus ISO 178:2001 |
2842MPa |
3300 MPa |
2906MPa |
86 MPa |
27 MPa |
|
Izod Impact Strength (notched) ISO 180:2000 |
10.5 KJ/m² |
3.1 KJ/m² |
2.1 KJ/m² |
No break |
No break |
|
Izod Impact Strength (unnotched) ISO 180:2000 |
67.2 KJ/m² |
9.7 KJ/m² |
5.7 KJ/m² |
No break |
No break |
FS 1088A - TPU | TPU powder
Specifications:
• Superb elongation
• Low processing temperature
• Stable size
• High recyclability
Application:
• Ideal for applications requiring a soft or flexible material
• Automotive interior, cushion, and flexible mechanical components
• Consumer goods such as shoeware, apparel, bag, helmet
Disclaimer:
Many factors may affect the performance characteristics of products. We recommend that you make tests to determine the suitability of a product for your particular purpose prior to use. Farsoon makes no warranties of any type, express or implied, including but not limited to, the warranties of merchantability or fitness for a particular use. This also applies regarding the consideration of possible intellectual property rights as well as laws and regulations.
Farsoon reserves the right to change the technical data without notice. Farsoon®, Buildstar®, Makestar® are registered trademarks of Farsoon Technologies.