FS Ti6Al4V
Titanium |
FS TA15
Titanium |
FS AlSi10Mg
Aluminum |
FS 18Ni300
Maraging Steel |
Density ( g/cm³) |
≥ 4.40 |
≥ 4.45 |
≥ 2.65 |
≥ 8.00 |
Mechanical Properties (As built) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
1150±70 |
1160±50 |
430±30 |
1150±100 |
Yield Strength(MPa) ISO6892-1 |
1000±50 |
n/a |
270±30 |
1050±100 |
Elongation after Fracture(%) ISO6892-1 |
8±2 |
8±2 |
3±1 |
12±3 |
Hardness HV ISO6507-1 / HRC ISO6508-1 |
360±30 HV5/15 |
n/a |
140±20 HV5/15 |
35±3 HRC |
Mechanical Properties1 (Heat treated) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
1050±70 |
1100±20 |
350±50 |
1950±100 |
Yield Strength(MPa) ISO6892-1 |
950±50 |
1040±20 |
240±30 |
1900±100 |
Elongation after Fracture(%) ISO6892-1 |
12±2 |
13±2 |
6±1 |
4±2 |
Hardness HV ISO6507-1 / HRC ISO6508-1 |
330±30 HV5/15 |
n/a |
75±20 HV5/15 |
53±3 HRC |
|
|
|
|
|
|
FS IN718
Inconel |
FS IN625
Inconel |
FS GH3536
Inconel |
|
Density ( g/cm³ ) |
≥8.18 |
≥ 8.40 |
≥ 8.30 |
|
Mechanical Properties (As built) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
1100±70 |
1000±70 |
820±70 |
|
Yield Strength(MPa) ISO6892-1 |
800±70 |
730±70 |
650±70 |
|
Elongation after Fracture(%) ISO6892-1 |
24±4 |
35±5 |
30±5 |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
300±20 HV5/15 |
270±10 HV5/15 |
270±5 HV5/15 |
|
Mechanical Properties1 (Heat treated) |
|
|
|
|
Tensile Strength(MPa)ISO6892-1 |
1350±100 |
1050±70 |
725±70 |
|
Yield Strength(MPa) ISO6892-1 |
n/a |
700±70 |
330±70 MPa |
|
Elongation after Fracture(%) ISO6892-1 |
16±4 |
35±5 |
43±5 |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
430±30 HV5/15 |
n/a |
n/a |
|
|
|
|
|
|
|
FS 420
Stainless Steel |
FS 15-5PH
Stainless Steel |
FS 17-4PH
Stainless Steel |
FS 316L
Stainless Steel |
Density ( g/cm³ ) |
≥ 7.70 |
≥ 7.76 |
≥ 7.70 |
≥ 7.90 |
Mechanical Properties (As built) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
≥1100 |
1200±100 |
1050±100 |
637±50 |
Yield Strength(MPa) ISO6892-1 |
900±100 |
725±100 |
900±100 |
550±50 |
Elongation after Fracture(%) ISO6892-1 |
≥ 2 |
16±4 |
16±4 |
34±5 |
Hardness HV ISO6507-1 / HRC ISO6508-1 |
48±3HRC |
32-37HRC |
n/a |
215±10 HV5/15 |
Mechanical Properties1 (Heat treated) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
1000±100 |
1450±100 |
n/a |
600±50 |
Yield Strength(MPa) ISO6892-1 |
n/a |
1130±100 |
n/a |
n/a |
Elongation after Fracture(%) ISO6892-1 |
17±5 |
14±3 |
n/a |
45±5 |
Hardness HV ISO6507-1 / HRC ISO6508-1 |
32±4HRC |
≥ 40HRC |
n/a |
190±10 HV5/15 |
|
|
|
|
|
|
FS CoCrMo
Cobalt Chrome |
FS CoCrMoW
Cobalt Chrome |
FS CuSn10
Bronze |
|
Density ( g/cm³) |
≥8.35 |
≥ 8.55 |
≥ 8.78 |
|
Mechanical Properties (As built) |
|
|
|
|
Tensile Strength(MPa) ISO6892-1 |
1150±100 |
1100±100 |
500±50 |
|
Yield Strength(MPa) ISO6892-1 |
900±100 |
900±100 |
380±40 |
|
Elongation after Fracture(%) ISO6892-1 |
10±2 |
10±2 |
30±10 |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
n/a |
n/a |
130±15 HV5/15 |
|
Mechanical Properties1 (Heat treated) |
|
|
|
|
Tensile Strength (MPa)ISO6892-1 |
1050±100 |
1100±100 |
n/a |
|
Yield Strength(MPa) ISO6892-1 |
n/a |
n/a |
n/a |
|
Elongation after Fracture(%) ISO6892-1 |
15±2 |
9±2 |
n/a |
|
Hardness HV ISO6507-1 / HRC ISO6508-1 |
n/a |
n/a |
n/a |
|