Your present location:　Home > Solutions > Polymer Materials > Ultrasint X028 | PA6 powder
Ultrasint X028 | PA6 powder

General Properties FS 3300PA PA1212-based powder FS 3300PA PA1212-based powder FS 3401GB
Glass bead filled		 FS 3400CF
Carbon fiber filled		 FS 3250MF
Mineral fiber filled		 FS 4100PA
PA11 powder
Bulk Density 0.45~0.55 g/cm³ 0.48 g/cm³ 0.67 g/cm³ 0.51 g/cm³ 0.55 g/cm³ 0.49 g/cm³
Part Density 0.96 g/cm³ 0.95 g/cm³ 1.26 g/cm³ 1.08-1.10 g/cm³ 1.20 g/cm³ 1.03 g/cm³
Color Black White Gray Black Light gray White
             
Thermal Properties            
Melting Point (10℃/min) ISO 11357.1:1997 179~185°C 183°C 184°C 184°C 183°C 203°C
Heat Deflection Temp(HDT) @1.82 MPa  ISO 75-2:2003 70~85°C 83.5°C 68.8°C 72 °C 129°C 49°C
Heat Deflection Temp(HDT) @0.45 MPa ISO 75-2:2003 135~155°C 146.2°C 152.4°C 168 °C 171°C 150°C
             
Mechanical Properties            
Tensile Strength ISO 527.2:1993 40~50 MPa 46 MPa 44 MPa 65-70 MPa 51 MPa 49 MPa
Tensile Modulus ISO 527.2:1993 1700~1900 MPa 1602 MPa 2644 MPa 4700-6500 MPa 6130 MPa 1542 MPa
Elongation at Break ISO 527.2:1993 5~20% 36% 9.3% 3.0-4.0% 5% 58%
Flexural Strength ISO 178:2001 36~45 MPa 46.3 MPa 60.3 MPa 94-113 MPa 76 MPa 60 MPa
Flexural Modulus ISO 178:2001 1000~1150 MPa 1300 MPa 2210 MPa 4500-5600 MPa 4633 MPa 1463 MPa
Izod Impact Strength (notched) ISO 180:2000 10~24 KJ/m² 4.9 KJ/m² 6.6 KJ/m² 4.3 KJ/m² 5.59 KJ/m² 25 KJ/m²
Izod Impact Strength (unnotched) ISO 180:2000 Tbd 13.2 KJ/m² 31.1 KJ/m² 16 KJ/m² 20.78 KJ/m² No break

General Properties Ultrasint X043
PA6 powder		 Ultrasint X028
PA6 powder		 FS 8100PPS
PPS powder		 FS 1092A-TPU
TPU powder		 FS 1088A-TPU
TPU powder
Bulk Density 0.52g/cm³ 0.52 g/cm³ 0.57 g/cm³ 0.64 g/cm³ 0.46 g/cm³
Part Density 1.14g/cm³ 1.15 g/cm³ 1.28 g/cm³ 1.12 g/cm³ 1.20 g/cm³
Color Black Light yellow Light yellow White White
           
Thermal Properties          
Melting Point (10℃/min) ISO 11357.1:1997 225°C 220°C 295°C 169°C 160°C
Heat Deflection Temp(HDT) @1.82 MPa  ISO 75-2:2003 93°C 100°C 116 °C n/a n/a
Heat Deflection Temp(HDT) @0.45 MPa  ISO 75-2:2003 191°C 199°C 220°C n/a n/a
           
Mechanical Properties          
Tensile Strength ISO 527.2:1993 74 MPa 78MPa 47 MPa 18 MPa 20 MPa
Tensile Modulus ISO 527.2:1993 3457 MPa 3550 MPa 3412 MPa 61 MPa 30MPa
Elongation at Break ISO 527.2:1993 4.0% 13.0% 3.8% 276% 340%
Flexural Strength ISO 178:2001 99 MPa 121 MPa 63 MPa 6.2 MPa n/a
Flexural Modulus ISO 178:2001 2842MPa 3300 MPa 2906MPa 86 MPa 27 MPa
Izod Impact Strength (notched) ISO 180:2000 10.5 KJ/m² 3.1 KJ/m² 2.1 KJ/m² No break No break
Izod Impact Strength (unnotched) ISO 180:2000 67.2 KJ/m² 9.7 KJ/m² 5.7 KJ/m² No break No break

 

Ultrasint X028 | PA6 powder

 

Specifications：
• Excellent mechanical properties and strength
• High resistance to thermal deformation
• Tensile strength exceeding most polyamides
• Good recyclability
• Excellent elastic modulus and stiffness
 

Application：
• Produce end-use functional parts with high mechanical properties and toughness
• Parts with strict requirements of geometry optimization and weight optimization in Aerospace & Aviation, automobile and consumer goods
• Rapid manufacturing for medium-volume or small-volume products

 

Disclaimer:
Many factors may affect the performance characteristics of products. We recommend that you make tests to determine the suitability of a product for your particular purpose prior to use. Farsoon makes no warranties of any type, express or implied, including but not limited to, the warranties of merchantability or fitness for a particular use. This also applies regarding the consideration of possible intellectual property rights as well as laws and regulations.
Farsoon reserves the right to change the technical data without notice. Farsoon®, Buildstar®, Makestar® are registered trademarks of Farsoon Technologies.
Last Change: 2019-06-20

 