Your present location: 首页 >> Solutions >> Polymer Materials >> FS3250MF | Mineral fiber filled
  • 产品名称: FS3250MF | Mineral fiber filled

General Properties     FS3300PA
PA1212-based powder
FS3300PA-F
PA12 powder
FS3201PA-F
PA12 powder
FS3401GB-F
Glass bead filled
Bulk Density     0.48 g/cm³ 0.52 g/cm³ 0.50 g/cm³ 0.65 g/cm³
Part Density     0.95 g/cm³ 1.02 g/cm³ 1.04 g/cm³ 1.30 g/cm³
Color     White Black Black Black
             
Thermal Properties            
Melting Point (10℃/min)  ISO 11357-1:2020     183°C 184°C 185.5°C 185.5°C
Heat Deflection Temp(HDT)@1.8 MPa  ISO 78-1:2020     83.5°C 53 °C 62°C 62°C
Heat Deflection Temp(HDT)@0.45 MPa ISO 78-1:2020     146.2°C 147 °C 147°C 157°C
             
Mechanical Properties            
Tensile Strength ISO 527-1:2019     46 MPa 48.2 MPa 44 MPa 47 MPa
Tensile Modulus ISO 527-1:2019     1602 MPa 1820 MPa 1500 MPa 2810 MPa
Elongation at Break ISO 527-1:2018     36% 22% 35% 8.7%
Flexural Strength ISO 178:2019     46.3 MPa 60.4 MPa 49 MPa 73 MPa
Flexural Modulus ISO 178:2019     1300 MPa 1640 MPa 1300 MPa 2550 MPa
Izod Impact Strength (notched) ISO 180:2019     4.9 KJ/ 8.0 KJ/ 6.0 KJ/m² 9.5 KJ/
Izod Impact Strength (unnotched) ISO 180:2019     13.2 KJ/ 20 KJ/ 31 KJ/ 23 KJ/

 

General Properties     FS1092A-TPU
TPU powder
FS1088A-TPU
TPU powder

LUVOSINT® TPU X92A-1064 WT,  TPU powder

FS3401GB

Glass bead filled

Bulk Density     0.64 g/cm³ 0.46 g/cm³ 0.46 g/cm³ 0.67 g/cm³
Part Density     1.12 g/cm³ 1.20 g/cm³ 1.20 g/cm³ 1.26 g/cm³
Color     White White Gray Gray
             
Thermal Properties            
Melting Point (10℃/min) ISO 11357-1:2020     169°C 160°C 160°C 184°C
Heat Deflection Temp(HDT) @1.8 MPa  ISO 78-1:2020     n/a n/a n/a 68.8°C
Heat Deflection Temp(HDT)@0.45 MPaISO 78-1:2020     n/a n/a n/a 152.4°C
             
Mechanical Properties            
Tensile Strength ISO 527-1:2019     18 MPa 20 MPa 20 MPa 44 MPa
Tensile Modulus ISO 527-1:2019     61 MPa 30 MPa n/a 2644 MPa
Elongation at Break ISO 527-1:2018     276% 340% 520% 9.3%
Flexural Strength ISO 178:2019     6.2 MPa n/a n/a 60.3 MPa
Flexural Modulus ISO 178:2019     86 MPa 27 MPa 27 MPa 2210 MPa
Izod Impact Strength (notched) ISO 180:2019     No break No break No break 6.6 KJ/
Izod Impact Strength (unnotched) ISO 180:2019     No break No break No break 31.1KJ/

 

General Properties     Ultrasint® PA6
PA6 powder

Ultrasint® PP nat 01        PP powder

FS3150CF
Carbon fiber filled
FS4100PA
PA11 powder
Bulk Density     0.52 g/cm³ 0.33 g/cm³ 0.52 g/cm³ 0.49 g/cm³
Part Density     1.15 g/cm³ 0.89 g/cm³ 1.07 g/cm³ 1.03 g/cm³
Color     Canary yellow White Black White
             
Thermal Properties            
Melting Point (10℃/min) ISO11357-1:2020     220°C 140°C 185.5°C 203°C
Heat Deflection Temp(HDT)@1.8 MPa  ISO 78-1:2020     103°C 62°C 152°C 49°C
Heat Deflection Temp(HDT)@0.45 MPaISO 78-1:2020     192°C 102°C 169°C 150°C
             
Mechanical Properties            
Tensile Strength ISO 527-1:2019     66 MPa 28 MPa 56 MPa 49 MPa
Tensile Modulus ISO 527-1:2019     3700 MPa 1400 MPa 3350 MPa 1542 MPa
Elongation at Break ISO 527-1:2018     2.0% 30% 6.9% 58%
Flexural Strength ISO 178:2019     n/a n/a 87 MPa 60 MPa
Flexural Modulus ISO 178:2019     3350 MPa 1250 MPa 2820 MPa 1463 MPa
Izod Impact Strength (notched) ISO 180:2019     2.6 KJ/ 3.5 KJ/ 7.2 KJ/m² 25 KJ/
Izod Impact Strength (unnotched) ISO 180:2019     7.2 KJ/ 24 KJ/ 14 KJ/ No break
General Properties     FS3250MF
Mineral fiber filled
FS6140GF
PA6 powder
FS8100PPS
PPS powder
 
Bulk Density     0.55 g/cm³ 0.63 g/cm³ 0.57 g/cm³  
Part Density     1.20 g/cm³ 1.14 g/cm³ 1.28 g/cm³  
Color     Light gray Black Canary yellow  
             
Thermal Properties            
Melting Point (10℃/min) ISO11357-1:2020     183°C 224°C 295°C  
Heat Deflection Temp(HDT)@1.8 MPa  ISO 78-1:2020     129°C 203°C 116°C  
Heat Deflection Temp(HDT)@0.45 MPa ISO 78-1:2020     171°C 219°C 220°C  
             
Mechanical Properties            
Tensile Strength ISO 527-1:2019     51 MPa 77 MPa 47 MPa  
Tensile Modulus ISO 527-1:2019     6130 MPa 6585 MPa 3412 MPa  
Elongation at Break ISO 527-1:2018     5% 1.7% 3.8%  
Flexural Strength ISO 178:2019     76 MPa 130 MPa 63 MPa  
Flexural Modulus ISO 178:2019     4633 MPa 6266 MPa 2906 MPa  
Izod Impact Strength (notched) ISO 180:2019     5.59 KJ/ 4.2 KJ/ 2.1 KJ/m²  
Izod Impact Strength (unnotched) ISO 180:2019     20.8 KJ/ 13.6 KJ/ 5.7 KJ/  

 

FS3250MF
Advanced Mineral Fiber Filled PA12 Material suits a wide range of Automotive Applications
 
Key Features:
 
> Excellent mechanical properties with mineral fiber
> High resistance to thermal deformation
> Excellent size-stability, low contractive rate
 
Example Applications:
 
> Perfect for functional end-use parts production
> Parts with high mechanical properties & heat resistance
> Applications in automotive engine cooling system
 
 
Disclaimer:
Many factors may affect the performance characteristics of products. We recommend that you make tests to determine the suitability of a product for your particular purpose prior to use. Farsoon makes no warranties of any type, express or implied, including but not limited to, the warranties of merchantability or fitness for a particular use. This also applies regarding the consideration of possible intellectual property rights as well as laws and regulations.