Your present location: 首页 >> Solutions >> Metal Materials >> Specialized Materials
  • 产品名称: Specialized Materials

  FS Ti6Al4V
Titanium
FS TA15
Titanium
FS AlSi10Mg
Aluminum
FS 18Ni300
Maraging Steel
Density ( g/cm³) ≥ 4.40 ≥ 4.45 ≥ 2.65 ≥ 8.00
Mechanical Properties (As built)        
Tensile Strength(MPa) ISO6892-1 1150±70 1160±50 430±30 1150±100
Yield Strength(MPa) ISO6892-1  1000±50 n/a 270±30 1050±100
Elongation after Fracture(%) ISO6892-1 8±2 8±2 3±1 12±3
Hardness HV ISO6507-1 / HRC ISO6508-1 360±30 HV5/15 n/a 140±20 HV5/15 35±3 HRC
Mechanical Properties1 (Heat treated)        
Tensile Strength(MPa) ISO6892-1 1050±70 1100±20 350±50 1950±100
Yield Strength(MPa) ISO6892-1 950±50 1040±20 240±30 1900±100
Elongation after Fracture(%) ISO6892-1 12±2 13±2 6±1 4±2
Hardness HV ISO6507-1 / HRC ISO6508-1 330±30 HV5/15 n/a 75±20 HV5/15 53±3 HRC
         
  FS IN718
Inconel
FS IN625
Inconel
FS GH3536
Inconel
 
Density ( g/cm³ ) ≥8.18 ≥ 8.40 ≥ 8.30  
Mechanical Properties (As built)        
Tensile Strength(MPa) ISO6892-1 1100±70 1000±70 820±70  
Yield Strength(MPa) ISO6892-1 800±70 730±70 650±70  
Elongation after Fracture(%) ISO6892-1 24±4 35±5 30±5  
Hardness HV ISO6507-1 / HRC ISO6508-1 300±20 HV5/15 270±10 HV5/15 270±5 HV5/15  
Mechanical Properties1 (Heat treated)        
Tensile Strength(MPa)ISO6892-1 1350±100 1050±70 725±70  
Yield Strength(MPa) ISO6892-1 n/a 700±70 330±70 MPa  
Elongation after Fracture(%) ISO6892-1 16±4 35±5 43±5  
Hardness HV ISO6507-1 / HRC ISO6508-1 430±30 HV5/15 n/a n/a  
         
  FS 420
Stainless Steel
FS 15-5PH
Stainless Steel
FS 17-4PH
Stainless Steel
FS 316L
Stainless Steel
Density ( g/cm³ ) ≥ 7.70 ≥ 7.76 ≥ 7.70 ≥ 7.90
Mechanical Properties (As built)        
Tensile Strength(MPa) ISO6892-1 ≥1100 1200±100 1050±100 637±50
Yield Strength(MPa) ISO6892-1 900±100 725±100 900±100 550±50
Elongation after Fracture(%) ISO6892-1 ≥ 2 16±4 16±4 34±5
Hardness HV ISO6507-1 / HRC ISO6508-1 48±3HRC 32-37HRC n/a 215±10 HV5/15
Mechanical Properties1 (Heat treated)        
Tensile Strength(MPa) ISO6892-1 1000±100 1450±100 n/a 600±50
Yield Strength(MPa) ISO6892-1 n/a 1130±100 n/a n/a
Elongation after Fracture(%) ISO6892-1 17±5 14±3 n/a 45±5
Hardness HV ISO6507-1 / HRC ISO6508-1 32±4HRC ≥ 40HRC n/a 190±10 HV5/15
         
  FS CoCrMo
Cobalt Chrome
FS CoCrMoW
Cobalt Chrome
FS CuSn10
Bronze
 
Density ( g/cm³) ≥8.35 ≥ 8.55 ≥ 8.78  
Mechanical Properties (As built)        
Tensile Strength(MPa) ISO6892-1 1150±100 1100±100 500±50  
Yield Strength(MPa) ISO6892-1 900±100 900±100 380±40  
Elongation after Fracture(%) ISO6892-1 10±2 10±2 30±10  
Hardness HV ISO6507-1 / HRC ISO6508-1 n/a n/a 130±15 HV5/15  
Mechanical Properties1 (Heat treated)        
Tensile Strength (MPa)ISO6892-1 1050±100 1100±100 n/a  
Yield Strength(MPa) ISO6892-1 n/a n/a n/a  
Elongation after Fracture(%) ISO6892-1 15±2 9±2 n/a  
Hardness HV ISO6507-1 / HRC ISO6508-1 n/a n/a n/a  

1 For more information on heat treatment process, please contact us directly.
Farsoon systems are open material platform. For special materials such as tungsten, tantalum and pure copper, please contact us with your inquiries and requirements.

 

Specialized Materials
For specialized materials such as Tungsten and Tantalum, please contact Farsoon with your inquires or requirements.

Farsoon Headquarter
Tel: 400-055-2155
Email: info@farsoon.com

Farsooon Americas
Tel: (512) 387-7224
Email: info@farsoonam.com
 

More Information